CLASSIFICATION
- AS/NZS ISO 17632-B-T554T15-OMA-N1-UH5
- AWS A5. 28 E80C-Ni1 H4
The FabCOR Edge Ni1 has virtually no silicon Deposits at weld bead tow lines, excellent gap bridging capabilities, higher deposition rates and trevel speeds that solid wire and good impact toughness at low temperature.
Suitable for high strength low alloy steels, single or multi-pass welding, structural fabrications, nickel-molybdenum steels, heavy equipment and weathering steels.
Virtually No Silicon Deposits At Weld Bead Toe Lines
Excellent Gap Bridging Capabilities
Higher Deposition Rates And Travel Speeds Than Solid Wire
Good Impact Toughness At Low Temperature
Reduces Clean-Up Time, Minimizes Risk Of Inclusions
Minimizes Burn-Through, Reduces Part Rejection
Increases Productivity, More Parts Per Hour
Resists Cracking In Severe Applications
Typical All Weld Metal Chemical Analysis | |||||
---|---|---|---|---|---|
C | Mn | Si | S | P | Ni |
0.05 | 1.10 | 0.57 | 0.011 | 0.013 | 1.00 |
Typical Diffusible Hydrogen | |
---|---|
Hydrogen Equipment | 75% Ar/25% CO2 |
Gas Chromatography | 2.1 ml/100g |
Typical All Weld Metal Mechanical Analysis (As Welded) | |
---|---|
Mechanical Tests | 75% Ar/25% CO2 |
Tensile Strength | 586 MPa |
Yield Strength | 503 MPa |
Elongation | 25% |
CVN Impact Values | 60J @ -45ºC |